Acrylic emulsion pressure-sensitive adhesives (PSAS) reinforced with layered silicate
Li, H; Yang, Y; Yu, YZ
2004
Source PublicationJOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
ISSN0169-4243
Volume18Issue:15-16Pages:1759-1770
AbstractComposite acrylic pressure-sensitive adhesives (PSAs) were synthesized by emulsion polymerization in the presence of montmorillonite (MMT). An examination with X-ray diffraction (XRD) and transmission electron microscopy (TEM) showed that both intercalated and exfoliated structures of MMT coexisted in the composites. It was demonstrated by X-ray photoelectron spectroscopy (XPS) that enrichment of the surface by the surfactant during drying of emulsion PSAs was depressed by the layered silicate. Significant improvements in storage modulus and cohesive strength were achieved by incorporation of MMT. The addition of only a small amount of MMT was enough to improve the adhesion properties of acrylic emulsion PSAs.
KeywordEmulsion Polymerization Pressure-sensitive Adhesives (Psas) Montmorillonite Adhesion Properties
Indexed BySCI
Language英语
WOS IDWOS:000227092000006
PublisherVSP BV
Citation statistics
Cited Times:23[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/82130
Collection中国科学院化学研究所
Corresponding AuthorYang, Y
AffiliationChinese Acad Sci, Inst Chem, Beijing 100080, Peoples R China
Recommended Citation
GB/T 7714
Li, H,Yang, Y,Yu, YZ. Acrylic emulsion pressure-sensitive adhesives (PSAS) reinforced with layered silicate[J]. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY,2004,18(15-16):1759-1770.
APA Li, H,Yang, Y,&Yu, YZ.(2004).Acrylic emulsion pressure-sensitive adhesives (PSAS) reinforced with layered silicate.JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY,18(15-16),1759-1770.
MLA Li, H,et al."Acrylic emulsion pressure-sensitive adhesives (PSAS) reinforced with layered silicate".JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY 18.15-16(2004):1759-1770.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, H]'s Articles
[Yang, Y]'s Articles
[Yu, YZ]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, H]'s Articles
[Yang, Y]'s Articles
[Yu, YZ]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, H]'s Articles
[Yang, Y]'s Articles
[Yu, YZ]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.