Quantized nanocrystalline CdTe thin films
Zhang, JB; Lin, Y; Liu, Y; Xiao, XR
2001-08-01
Source PublicationCHINESE CHEMICAL LETTERS
ISSN1001-8417
Volume12Issue:8Pages:751-752
AbstractNanocrystalline CdTe thin films were prepared by asymmetric rectangular pulse electrodeposition in organic solution at 110 degreesC. STM image shows a porous network morphology constructed by interconnected spherical CdTe crystallites with a mean diameter of 4.2 nm. A pronounced size quantization was indicated in the action and absorption spectra. Potentials dependence dual conductive behavior was revealed in the photocurrent-potential (I-V) curves.
KeywordNanocrystalline Cdte Thin Film Asymmetric Rectangular Pulse Electrodeposition Size Quantization Dual Conductive Behavior
Indexed BySCI
Language英语
WOS IDWOS:000170303900029
PublisherCHINESE CHEMICAL SOCIETY
Citation statistics
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/77846
Collection中国科学院化学研究所
AffiliationChinese Acad Sci, Inst Chem, Ctr Mol Sci, Beijing 100080, Peoples R China
Recommended Citation
GB/T 7714
Zhang, JB,Lin, Y,Liu, Y,et al. Quantized nanocrystalline CdTe thin films[J]. CHINESE CHEMICAL LETTERS,2001,12(8):751-752.
APA Zhang, JB,Lin, Y,Liu, Y,&Xiao, XR.(2001).Quantized nanocrystalline CdTe thin films.CHINESE CHEMICAL LETTERS,12(8),751-752.
MLA Zhang, JB,et al."Quantized nanocrystalline CdTe thin films".CHINESE CHEMICAL LETTERS 12.8(2001):751-752.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, JB]'s Articles
[Lin, Y]'s Articles
[Liu, Y]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, JB]'s Articles
[Lin, Y]'s Articles
[Liu, Y]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, JB]'s Articles
[Lin, Y]'s Articles
[Liu, Y]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.