Synthesis and characterization of phenyl-capped oligoanilines
Sun, ZC; Jing, XB; Wang, XH; Li, J; Wang, FS
Source PublicationSYNTHETIC METALS
AbstractA series of phenyl-capped oligoanilines were prepared by chemical oxidation coupling. By comparing the FTIR spectra of fully reduced oligoanilines with those of oxidized oligoanilines, the intensity ratio of 1600cm(-1) to 1500cm(-1) was correlated to the content of the quinoid rings in the oligomer. In UV-Vis spectra of the oligoanilines in their oxidized state, the maximum absorption near 600nm redshifted from 540nm to 610nm with increasing polarity of the solvent, indicating the existence of tautomers in oxidized oilgoanilines.
KeywordPhenyl-capped Oligoanilines Coupling Reaction Ftir Spectroscopy Uv-vis Absorption
Indexed ByISTP ; SCI
WOS IDWOS:000168741500183
Citation statistics
Cited Times:4[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Corresponding AuthorJing, XB
AffiliationChinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China
Recommended Citation
GB/T 7714
Sun, ZC,Jing, XB,Wang, XH,et al. Synthesis and characterization of phenyl-capped oligoanilines[J]. SYNTHETIC METALS,2001,119(1-3):399-400.
APA Sun, ZC,Jing, XB,Wang, XH,Li, J,&Wang, FS.(2001).Synthesis and characterization of phenyl-capped oligoanilines.SYNTHETIC METALS,119(1-3),399-400.
MLA Sun, ZC,et al."Synthesis and characterization of phenyl-capped oligoanilines".SYNTHETIC METALS 119.1-3(2001):399-400.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Sun, ZC]'s Articles
[Jing, XB]'s Articles
[Wang, XH]'s Articles
Baidu academic
Similar articles in Baidu academic
[Sun, ZC]'s Articles
[Jing, XB]'s Articles
[Wang, XH]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Sun, ZC]'s Articles
[Jing, XB]'s Articles
[Wang, XH]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.