Crystallization segregation DSC studies of PP/PE copolymers
Ma, Y; Wang, Y; Zhu, SN; Xu, M
2001
Source PublicationCHINESE JOURNAL OF POLYMER SCIENCE
ISSN0256-7679
Volume19Issue:1Pages:93-96
AbstractThe structural analysis of two PP/PE copolymer samples, 1 and 2, was conducted by using C-13-NMR, GPC and crystallization segregation DSC (CSDSC) techniques. A pure polypropylene sample was also used for comparison. It was found that the two copolymer samples are very close in composition (the ethylene mol content is 4.3% and 4.5%, respectively), stereoregularity (96% and 97%) and molecular weight (M-w = 7.0 x 10(4) and 7.3 x 10(4); M-w/M-n = 5.0 and 6.1, respectively). While the CSDSC thermograms of the two samples are quite different from each other. Sample 1 shows a higher average melting temperature and a broader distribution of its thermogram These phenomena were explained as an indication of a less uniform distribution of ethylene units along the PP chains for sample 1. It was noted that CSDSC is a very sensitive and convenient technique for structural studies of copolymers.
KeywordPp/pe Copolymer Sequence Distribution Crystallization Segregation Dsc C-13-nmr
Indexed BySCI
Language英语
WOS IDWOS:000166329700016
PublisherSPRINGER-VERLAG BERLIN
Citation statistics
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/77630
Collection中国科学院化学研究所
Corresponding AuthorXu, M
AffiliationChinese Acad Sci, Inst Chem, Ctr Mol Sci, State Key Lab Polymer Phys & Chem, Beijing 100080, Peoples R China
Recommended Citation
GB/T 7714
Ma, Y,Wang, Y,Zhu, SN,et al. Crystallization segregation DSC studies of PP/PE copolymers[J]. CHINESE JOURNAL OF POLYMER SCIENCE,2001,19(1):93-96.
APA Ma, Y,Wang, Y,Zhu, SN,&Xu, M.(2001).Crystallization segregation DSC studies of PP/PE copolymers.CHINESE JOURNAL OF POLYMER SCIENCE,19(1),93-96.
MLA Ma, Y,et al."Crystallization segregation DSC studies of PP/PE copolymers".CHINESE JOURNAL OF POLYMER SCIENCE 19.1(2001):93-96.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Ma, Y]'s Articles
[Wang, Y]'s Articles
[Zhu, SN]'s Articles
Baidu academic
Similar articles in Baidu academic
[Ma, Y]'s Articles
[Wang, Y]'s Articles
[Zhu, SN]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Ma, Y]'s Articles
[Wang, Y]'s Articles
[Zhu, SN]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.