Crystal transitions of Nylon 11 under drawing and annealing
Zhang, QX; Mo, ZS; Zhang, HF; Liu, SY; Cheng, SZD
2001-06-01
Source PublicationPOLYMER
ISSN0032-3861
Volume42Issue:13Pages:5543-5547
AbstractThe crystal transitions of Nylon 11 annealed and drawn at different temperatures (T-d) with different drawing ratios (n) were investigated by wide-angle X-ray diffraction (WAXD). The alpha -form of Nylon Il could be transformed from the delta'-form by annealing at high temperature, The results showed that the crystal transitions of Nylon 11 strongly depended on the thermal history and the conditions of drawing. The delta'-form Nylon Il could he gradually transformed into the alpha -form when it was drawn at high temperature and the alpha -form was only partly transformed into the delta'-form when it was drawn at low temperature. This should be due to the effect of the competition between thermal inducement and drawing inducement. The thermal inducement was favorable to producing the alpha -form, while the drawing inducement was favorable to producing the delta'-form. (C) 2001 Elsevier Science Ltd. All rights reserved.
KeywordNylon 11 Crystal Transition Waxd
Indexed BySCI
Language英语
WOS IDWOS:000167896200005
PublisherELSEVIER SCI LTD
Citation statistics
Cited Times:82[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/77494
Collection中国科学院化学研究所
Corresponding AuthorMo, ZS
Affiliation1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China
2.Univ Akron, Inst Polymer Sci, Akron, OH 44325 USA
Recommended Citation
GB/T 7714
Zhang, QX,Mo, ZS,Zhang, HF,et al. Crystal transitions of Nylon 11 under drawing and annealing[J]. POLYMER,2001,42(13):5543-5547.
APA Zhang, QX,Mo, ZS,Zhang, HF,Liu, SY,&Cheng, SZD.(2001).Crystal transitions of Nylon 11 under drawing and annealing.POLYMER,42(13),5543-5547.
MLA Zhang, QX,et al."Crystal transitions of Nylon 11 under drawing and annealing".POLYMER 42.13(2001):5543-5547.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, QX]'s Articles
[Mo, ZS]'s Articles
[Zhang, HF]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, QX]'s Articles
[Mo, ZS]'s Articles
[Zhang, HF]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, QX]'s Articles
[Mo, ZS]'s Articles
[Zhang, HF]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.