Template effects of the ordered film formed from monodispersed polystyrene latex
Yang, ZZ; Qi, K; Liu, ZP; Wang, LJ; Zhao, DL
2000-06-01
Source PublicationACTA POLYMERICA SINICA
ISSN1000-3304
Issue3Pages:364-367
AbstractA method for preparing 3D ordered macroporous silicate materials was developed by using the ordered stacking structure of monodispersed polystyrene latex as a template. By using a modified sol-gel procedure, the ordered template was permeated and filled with silicate, and the title porous materials was formed after removing the template by calcination at high temperature. Moreover, the pores were highly ordered throughout all the sample. After observing the morphological profile of the sample before calcination, it was found that silicate existed in two typical morphologies: monodispersed particles in the cavities and interconnected network within the interstice of the template. The transition morphology was rod-like formed by the condensation of the silicate monodispersed particles. Two aspects concerning with the template effects of the ordered latex film were emphasized: the polymeric spheres may result in orderly packed holes after calcination, and the dielectric interfacial layer surrounding the polymeric spheres may induce the formation of monodispersed silicate spheres with ordered stacking. Both aspects played important roles in the formation of the highly ordered inorganic porous materials by calcination the gel at high temperature.
KeywordMonodispersed Polystyrene Latex Ordered Latex Film Template Effects Sol-gel Procedure
Indexed BySCI
Language英语
WOS IDWOS:000087933500024
PublisherSCIENCE PRESS
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/76398
Collection中国科学院化学研究所
Corresponding AuthorYang, ZZ
Affiliation1.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Polymer Phys Lab, Beijing 100080, Peoples R China
2.Beijing Normal Univ, Dept Chem, Beijing 1000875, Peoples R China
Recommended Citation
GB/T 7714
Yang, ZZ,Qi, K,Liu, ZP,et al. Template effects of the ordered film formed from monodispersed polystyrene latex[J]. ACTA POLYMERICA SINICA,2000(3):364-367.
APA Yang, ZZ,Qi, K,Liu, ZP,Wang, LJ,&Zhao, DL.(2000).Template effects of the ordered film formed from monodispersed polystyrene latex.ACTA POLYMERICA SINICA(3),364-367.
MLA Yang, ZZ,et al."Template effects of the ordered film formed from monodispersed polystyrene latex".ACTA POLYMERICA SINICA .3(2000):364-367.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yang, ZZ]'s Articles
[Qi, K]'s Articles
[Liu, ZP]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yang, ZZ]'s Articles
[Qi, K]'s Articles
[Liu, ZP]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yang, ZZ]'s Articles
[Qi, K]'s Articles
[Liu, ZP]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.