Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier
Yu, ZZ; Lei, M; Ou, YC; Yang, GS
2000-06-01
Source PublicationACTA POLYMERICA SINICA
ISSN1000-3304
Issue3Pages:275-279
AbstractA maleited impact modifier (TPEg) with polyethylene-octene rubber shell and semi-crystalline polymer core was used to toughen non-crystalline copolyester (PETG) resin. TPEg has a significant toughening effect on PETG. A sharp transition from brittle to super-tough states for PETG/TPEg blends occurred when the TPEg content was up to 10%. Although the maleited polyethylene-octene rubber (POEg) also results in a brittletough transition, this transition takes place at a higher POEg content indicating that the loss of thensile strength and modulus of PETG blends in more serious. The effects of TPEg on impact toughness of PETG blends are well reflected from their evolution processes of topography and morphology formed during the impact fracture testing. The impact fractured surface of PETG blend with 5 wt% TPEg exhibits a very small area of its slow crack growth region and feather-like markings in its fast crack growth region under low magnification, indicating a brittle appearance. Whereas the impact fractured surface of PETG blend with 10wt% TPEg exhibits a very large area of its slow crack growth region and some parabola-like markings in its fast crack growth region under low magnification. Moreover, an extensive shear yielding of matrix can be seen both in the slow and the fast crack growth regions of the PETG/TPEg(90/10) blend under high magnification. It may dissipate a significant amount of impact energy,thereby responsible for the super toughness.
KeywordToughness Morphology Blends Copolyester Impact Modifier
Indexed BySCI
Language英语
WOS IDWOS:000087933500005
PublisherSCIENCE PRESS
Citation statistics
Cited Times:2[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/76326
Collection中国科学院化学研究所
Corresponding AuthorYu, ZZ
AffiliationChinese Acad Sci, Inst Chem, Ctr Mol Sci, State Key Lab Engn Plast, Beijing 100080, Peoples R China
Recommended Citation
GB/T 7714
Yu, ZZ,Lei, M,Ou, YC,et al. Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier[J]. ACTA POLYMERICA SINICA,2000(3):275-279.
APA Yu, ZZ,Lei, M,Ou, YC,&Yang, GS.(2000).Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier.ACTA POLYMERICA SINICA(3),275-279.
MLA Yu, ZZ,et al."Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier".ACTA POLYMERICA SINICA .3(2000):275-279.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yu, ZZ]'s Articles
[Lei, M]'s Articles
[Ou, YC]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yu, ZZ]'s Articles
[Lei, M]'s Articles
[Ou, YC]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yu, ZZ]'s Articles
[Lei, M]'s Articles
[Ou, YC]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.