Rheological and mechanical properties of poly(butylene terephthalate)-modified epoxy resins
Wang, X; Li, YM; Yu, YZ
1997
Source PublicationJOURNAL OF MATERIALS SCIENCE
ISSN0022-2461
Volume32Issue:1Pages:111-114
AbstractPoly(butylene terephthalate) (PBT) was used as modifier for epoxy resin. With the incorporation of 7.5 wt% PBT, the resin became a gel as shown by rheological measurements in steady shear, thixotropic loop and dynamic shear mode. The gel was very stable on storage. An abrupt change of rheological properties occurred at the dissolution temperature of the PBT spherulites. The PBT modifier did not impair mechanical properties of the cured resins, yet a moderate improvement in toughness was achieved.
Indexed BySCI
Language英语
WOS IDWOS:A1997WC32500014
PublisherSPRINGER
Citation statistics
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/74142
Collection中国科学院化学研究所
AffiliationACAD SINICA, INST CHEM, BEIJING 100080, PEOPLES R CHINA
Recommended Citation
GB/T 7714
Wang, X,Li, YM,Yu, YZ. Rheological and mechanical properties of poly(butylene terephthalate)-modified epoxy resins[J]. JOURNAL OF MATERIALS SCIENCE,1997,32(1):111-114.
APA Wang, X,Li, YM,&Yu, YZ.(1997).Rheological and mechanical properties of poly(butylene terephthalate)-modified epoxy resins.JOURNAL OF MATERIALS SCIENCE,32(1),111-114.
MLA Wang, X,et al."Rheological and mechanical properties of poly(butylene terephthalate)-modified epoxy resins".JOURNAL OF MATERIALS SCIENCE 32.1(1997):111-114.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, X]'s Articles
[Li, YM]'s Articles
[Yu, YZ]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, X]'s Articles
[Li, YM]'s Articles
[Yu, YZ]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, X]'s Articles
[Li, YM]'s Articles
[Yu, YZ]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.