Y2SiO5:Ce3+ particle growth during sol-gel preparation
Li Xiujuan1,2; Jiao Huan1,3; Wang Xiaoming1; Zeng Zhengzhi2; Jing Xiping1
2010-08-01
Source PublicationJOURNAL OF RARE EARTHS
ISSN1002-0721
Volume28Issue:4Pages:504-508
AbstractThe phosphor Y2SiO5:Ce3+ was prepared by a sol-gel method and the particle growth process was investigated by XRD, SEM and TEM. After heating at 400 degrees C, the as-dried gel became a powder composed of mixed phases of polycrystalline Y2O3 and amorphous SiO2. With an increase in temperature, the crystallinity of Y2O3 improved. The sample quickly changed to the pure Y2SiO5 phase when it was heated at 1400 degrees C for 10 min. SEM indicated that the as-dried gel consisted of large porous particles. At an annealing temperature of higher than 400 degrees C, the pores in the large particles gradually expanded and grains started to appear. Consequently, the large particles disintegrated into small particles. When the sample was heated at 1400 degrees C, we obtained fine phosphor particles (around 2 mu m) with smooth surfaces. The optimized condition for the preparation of the Y2SiO5:Ce3+ phosphor was to heat at 1400 degrees C for 2 h.
KeywordOptical Materials Morphology Luminescence Sol-gel Chemistry Rare Earths
DOI10.1016/S1002-0721(09)60141-1
Indexed BySCI
Language英语
WOS IDWOS:000281513500005
PublisherELSEVIER SCIENCE BV
Citation statistics
Cited Times:7[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/71208
Collection中国科学院化学研究所
Corresponding AuthorJing Xiping
Affiliation1.Peking Univ, Beijing Natl Lab Mol Sci, State Key Lab Rare Earth Mat Chem & Applicat, Coll Chem & Mol Engn, Beijing 100871, Peoples R China
2.Lanzhou Univ, Coll Chem & Chem Engn, Lanzhou 730000, Peoples R China
3.Shaanxi Normal Univ, Sch Chem & Mat Sci, Key Lab Macromol Sci Shaanxi Prov, Xian 710062, Peoples R China
Recommended Citation
GB/T 7714
Li Xiujuan,Jiao Huan,Wang Xiaoming,et al. Y2SiO5:Ce3+ particle growth during sol-gel preparation[J]. JOURNAL OF RARE EARTHS,2010,28(4):504-508.
APA Li Xiujuan,Jiao Huan,Wang Xiaoming,Zeng Zhengzhi,&Jing Xiping.(2010).Y2SiO5:Ce3+ particle growth during sol-gel preparation.JOURNAL OF RARE EARTHS,28(4),504-508.
MLA Li Xiujuan,et al."Y2SiO5:Ce3+ particle growth during sol-gel preparation".JOURNAL OF RARE EARTHS 28.4(2010):504-508.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li Xiujuan]'s Articles
[Jiao Huan]'s Articles
[Wang Xiaoming]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li Xiujuan]'s Articles
[Jiao Huan]'s Articles
[Wang Xiaoming]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li Xiujuan]'s Articles
[Jiao Huan]'s Articles
[Wang Xiaoming]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.