Investigations on iron sulfide nanosheets prepared via a single-source precursor approach
Han, Wei; Gao, Mingyuan
2008-03-01
Source PublicationCRYSTAL GROWTH & DESIGN
ISSN1528-7483
Volume8Issue:3Pages:1023-1030
AbstractTwo-dimensional (2D) magnetic pyrrhotite (Fe(7)S(8)) and greigite (Fe(3)S(4)) nanosheets were synthesized by pyrolyzing, respectively, single-source precursors such as Fe(DdtC)(2)(Phen) (Phen = 1,10-phenanthroline; Ddtc = diethyldithiocarbamate) and Fe(DdtC)(3) in oleylamine. Under optimized reaction temperature of 280 degrees C, both monoclinic Fe(7)S(8) and cubic Fe(3)S(4) obtained presented hexagonal sheet structure with sizes of 500-800 nm and 100-500 nm, respectively. AFM measurements revealed that both of these two types of nanosheets had a nearly identical thickness of 50 nm. Further XRD measurements revealed that the reaction temperature played a critical role in determining the crystalline structure as well as the chemical composition of the resultant nanosheets. In the reaction temperature range of 240-320 degrees C, a higher reaction temperature generally favored the transformations of monoclinic Fe(7)S(8) to hexagonal FeS, and cubic Fe(3)S(4) to hexagonal Fe(7)S(8), respectively. The magnetic properties of the resultant nanosheets were accordingly altered against the reaction temperature. Further experimental results obtained by combining different types of solvents suggested that oleylamine was necessary for the formation of hexagonal Fe(7)S(8) nanosheets. In contrast, it only helped prevent the hexagonal Fe(3)S(4)nanosheets from agglomeration. It was also found that both pyrrhotite (Fe(7)S(8)) and greigite (Fe(3)S(4)) nanosheets were metastable under ambient conditions. Systematic XPS measurements were carried out to investigate the air stabilities of the resultant nanosheets.
DOI10.1021/cg701075u
Indexed BySCI
Language英语
WOS IDWOS:000253800200045
PublisherAMER CHEMICAL SOC
Citation statistics
Cited Times:90[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.iccas.ac.cn/handle/121111/65604
Collection中国科学院化学研究所
Corresponding AuthorGao, Mingyuan
AffiliationChinese Acad Sci, Inst Chem, Key Lab Colloid Interface Sci & Chem Thermodynam, Beijing 100080, Peoples R China
Recommended Citation
GB/T 7714
Han, Wei,Gao, Mingyuan. Investigations on iron sulfide nanosheets prepared via a single-source precursor approach[J]. CRYSTAL GROWTH & DESIGN,2008,8(3):1023-1030.
APA Han, Wei,&Gao, Mingyuan.(2008).Investigations on iron sulfide nanosheets prepared via a single-source precursor approach.CRYSTAL GROWTH & DESIGN,8(3),1023-1030.
MLA Han, Wei,et al."Investigations on iron sulfide nanosheets prepared via a single-source precursor approach".CRYSTAL GROWTH & DESIGN 8.3(2008):1023-1030.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Han, Wei]'s Articles
[Gao, Mingyuan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Han, Wei]'s Articles
[Gao, Mingyuan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Han, Wei]'s Articles
[Gao, Mingyuan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.